- Classifications
- CSA W48 : B-G 49A 3 C1 S6
EN ISO 14341-A : G 3Si1
EN ISO 14341-A : G 38 3 C1 3Si1
EN ISO 14341-A : G 42 4 M20 3Si1
EN ISO 14341-A : G 42 4 M21 3Si1
JIS Z 3312 : YGW 12(C1)
SFA/AWS A5.18 : ER70S-6 - Approvals
- ABS : 3Y SA
BV : SA3YM
CE : EN 13479
CWB : B-G 49A 3 C1 S6
DB : 42.039.29
DNV-GL : III YMS
JIS : YGW12 (C1)
LR : 3YS H15
NAKS/HAKC : 1.0-1.6 mm
NAKS/HAKC : 1.2-1.6 mm
PRS : 3YS (C1, M21)
RINA : 3Y S
UKCA : EN 13479
VdTÜV : 10052 - Alloy Type
- Carbon-manganese steel (Mn/Si-alloyed)
- Shielding Gas
- M20, M21, C1 (EN ISO 14175)
- Packaging
- 1.2mm / 18kg
- Diameter (Ø)
- 1.2 mm
Suvirinimo viela ESAB OK AristoRod 12.50 - 1.2mm / 18kg
1263772
Price
€81.52
VAT incl.
Stock Quantity:
Kaunas Shop
not available
In our warehouse
(5+ pcs)
Delivery terms:
FREE pick up thursday, april 30 d., in the store, Raudondvario pl. 141, Kaunas
(€0.00)
We will deliver the product to you via: 2-4 w.d. Venipak
(€6.00)
We will deliver the product to you via: 2-4 w.d. Venipak pickup (paštomatas)
(€8.00)
Description
The non copper coated OK AristoRod 12.50 is a manganese-silicon alloyed solid wire for GMAW of unalloyed steels, such as general structural, pressure vessel, ship building and for fine-grained carbon-manganese steels for the same purpose with a minimum yield strength of max 420 MPa. The electrode can be welded with either a gas mixture or with pure CO2 as the shielding gas. The AristoRod wires are suitable for operating at high currents with maintained disturbance free wire feeding giving a stable arc with a low amount of spatter. OK AristoRod 12.50 delivered in the unique Esab Octagonal Marathon Pac is excellent in mechanised welding applications.
Specifications
Approvals are based on factory location. Please contact ESAB for more information.
| Typical Tensile Properties | |||
|---|---|---|---|
| Condition | Yield Strength | Tensile Strength | Elongation |
| AWS C1 | |||
| As Welded | 430 MPa | 530 MPa | 30 % |
| EN C1 | |||
| As Welded | 440 MPa | 540 MPa | 25 % |
| EN M21 | |||
| As Welded | 470 MPa | 560 MPa | 26 % |
| Stress Relieved 15 hour(s) 620 °C | 370 MPa | 495 MPa | 28 % |
| Typical Charpy V-Notch Properties | ||
|---|---|---|
| Condition | Testing Temperature | Impact Value |
| AWS C1 | ||
| As Welded | -30 °C | 75 J |
| EN C1 | ||
| As Welded | -30 °C | 75 J |
| As Welded | 20 °C | 110 J |
| EN M21 | ||
| Stress Relieved | -20 °C | 90 J |
| Stress Relieved | 20 °C | 120 J |
| As Welded | -20 °C | 120 J |
| As Welded | -40 °C | 90 J |
| As Welded | -30 °C | 100 J |
| As Welded | -50 °C | 70 J |
| As Welded | 20 °C | 130 J |
| Typical Weld Metal Analysis % | ||||||
|---|---|---|---|---|---|---|
| C | Mn | Si | S | P | Cu | Ti+Zr |
| C1 | ||||||
| M21 | ||||||
| 0.08 | 0.94 | 0.63 | 0.012 | 0.013 | 0,07 | - |
| Typical Wire Composition % | ||
|---|---|---|
| C | Mn | Si |
| 0.08 | 1.46 | 0.85 |
| Deposition Data | ||||
|---|---|---|---|---|
| Diameter | Current | Voltage | Wire Feed Speed | Deposition Rate |
| 0.8 mm | 60-200 A | 18-24 V | 3.2-10.0 m/min | 0.8-2.3 kg/h |
| 0.9 mm | 70-250 A | 18-26 V | 3.0-12.0 m/min | 0.9-3.5 kg/h |
| 1.0 mm | 80-300 A | 18-32 V | 2.7-15.0 m/min | 1.0-5.5 kg/h |
| 1.14 mm | 100-350 A | 18-34 V | 2.6-15.0 m/min | 1.2-7.0 kg/h |
| 1.2 mm | 120-380 A | 18-35 V | 2.5-15.0 m/min | 1.3-8.0 kg/h |
| 1.32 mm | 130-400 A | 19-35 V | 2.4-15.0 m/min | 1.5-8.5 kg/h |
| 1.4 mm | 150-420 A | 22-36 V | 2.3-12.0 m/min | 1.6-8.7 kg/h |
| 1.6 mm | 225-550 A | 28-38 V | 2.3-10.0 m/min | 2.1-9.4 kg/h |
| 2.0 mm | 300-650 A | 32-44 V | 3.0-7.0 m/min | 4.4-10.2 kg/h |